This work presents the effect of elliptical defects orientation on the durability of specimens made of C45 steel. Three kinds of specimens with elliptical defects in the form of a one-sided notch oriented at different angles 45, 60, and 90 degrees were subjected to cyclic bending (R=-1). The stress state analysis was performed using local and non-local methods to determine an equivalent amplitude of stress, and then the results...

Cold-spray coatings were produced by FeCoCrNiMn high-entropy alloy powders deposited on carbon steel substrate. The coatings were realized at intermediate temperature and high pressure (at 1100 °C and 7 MPa). The coating microstructure was characterized by scanning electron microscopy and X-ray diffraction, revealing a very dense deposition and high flattening ratio of the splatted particles. This had a large influence on the...

eCoCrNiMn high entropy alloy powders were employed to produce coatings on carbon steel through high pressure cold spray (at 1100 °C and 7 MPa in temperature and pressure respectively). X-ray diffraction of the sprayed material revealed a dense coating with the retention of the original crystallographic structure. Once splatted, particles revealed high flattening ratio with consequent excellent adhesion of the coating to the substrate....

The influence of defect features on fatigue behaviour is a complex trivial issue. Although the important advances over the last decades, the dialectical relationship between the defect orientation and durability is not clearly understood. The paper aims at studying the influence of the orientation of elliptical defects on the durability of samples made of C45 steel. Three types of samples with elliptical defects were subjected...

This paper studies the fatigue crack initiation and fatigue crack propagation of notched cylindrical bars made of 7050-T6 aluminium alloy subjected to multiaxial bending-torsion loading. The sites of crack initiation and the angles of crack initiation were successfully predicted from the distribution of the first principal stress at the notch surface. Fatigue crack initiation lives were computed through the new concept of energy...