In this paper, the entire fracture surface approach was used to assess an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the fatigue response of 10H2M (10CrMo9–10) power engineering steel. The mechanical testing was carried out on the hourglass specimens produced from the as-received, unused pipeline and the same material after long-time exploitation. The uniaxial tensile...

The objectives of this study were to investigate the fracture surface topography of X8CrNiS18-9 austenitic stainless-steel specimens for different loadings and notch radii and to supplement the knowledge about the fracture mechanisms for fatigue performance. Cases with three different values of the notch radius ρ and the stress amplitude σa were analysed. The fracture topographies were quantified by the areas over their entire...

The paper studies the effect of strain-loading sequence on fatigue lifetime and fracture surface topographies in 7075-T651 aluminum alloy specimens. Fatigue tests were performed in two ways: (i) constant-amplitude loading and (ii) two series of variable amplitude loading with non-zero mean strain values. The topography of the fatigue fractures was measured over their entire surfaces with the help of an optical confocal measurement...

This paper presents the experimental results of a study investigating the effect of holes and notches made on the overlap ends on the strength of adhesive joints. Single-lap joints made of S235JR steel sheets bonded with Araldite 2024-2 epoxy adhesive were tested. For comparative reasons, static shear strength tests and high-cycle fatigue strength tests were performed. Adhesive-filled joints having three holes, each with a diameter...