Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens
Abstract
The objectives of this study were to investigate the fracture surface topography of X8CrNiS18-9 austenitic stainless-steel specimens for different loadings and notch radii and to supplement the knowledge about the fracture mechanisms for fatigue performance. Cases with three different values of the notch radius ρ and the stress amplitude σa were analysed. The fracture topographies were quantified by the areas over their entire surfaces with the aid of an optical confocal measurement system. The results showed a well-correlated root mean square height Sq and void volume Vv, identifying the characteristics of the entire fracture method. A fracture surface topography fatigue damage model was developed based on the product of the stress amplitude σa by the Sq to the Vv ratio. Overall, the predictions were close to the fatigue lives found in the experiments.
Citations
-
2 8
CrossRef
-
0
Web of Science
-
2 7
Scopus
Authors (4)
-
Grzegorz Robak
-
Krzysztof Żak
-
Ricardo Branco
Cite as
Full text
- Publication version
- Accepted or Published Version
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.engfailanal.2022.106121
- License
-
open in new tab
Keywords
Details
- Category:
- Articles
- Type:
- artykuły w czasopismach
- Published in:
-
ENGINEERING FAILURE ANALYSIS
no. 135,
ISSN: 1350-6307 - Language:
- English
- Publication year:
- 2022
- Bibliographic description:
- Macek W., Robak G., Żak K., Branco R.: Fracture surface topography investigation and fatigue life assessment of notched austenitic steel specimens// ENGINEERING FAILURE ANALYSIS -Vol. 135, (2022), s.106121-
- DOI:
- Digital Object Identifier (open in new tab) 10.1016/j.engfailanal.2022.106121
- Sources of funding:
-
- Free publication
- Verified by:
- Gdańsk University of Technology
seen 124 times
Recommended for you
Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load
- W. Macek,
- D. Rozumek,
- S. Faszynka
- + 3 authors
Effect of bending-torsion on fracture and fatigue life for 18Ni300 steel specimens produced by SLM
- W. Macek,
- R. Masoudi Nejad,
- S. Zhu
- + 5 authors
Fatigue fracture surface metrology of thin-walled tubular austenitic steel specimens after asynchronous loadings
- W. Macek,
- Ł. Pejkowski,
- R. Branco
- + 2 authors