In this paper, the structural properties and the electrical conductivity of La1−xPrxNbO4+δ (x = 0.00, 0.05, 0.1, 0.15, 0.2, 0.3) and PrNbO4+δ are presented and discussed. All synthesized samples crystallized in a monoclinic structure with similar thermal expansion coefficients. The phase transition temperature between the monoclinic and tetragonal structure increases with increasing praseodymium content from 500 ◦C for undoped...

The results of ionic transport and structural measurements for the lanthanum orthoniobate doped by praseodymium are presented and discussed. The influence of calcium co-doping on these properties has also been analyzed. The results suggest the predominant protonic conductivity for the investigated system in the whole range of investigated temperatures. The influence of calcium co-doping on phase purity is analyzed.

The results of electrical conductivity studies, structural measurements and thermogravimetric analysis of La1−xTbxNbO4+δ (x = 0.00, 0.05, 0.1, 0.15, 0.2, 0.3) are presented and discussed. The phase transition temperatures, measured by high-temperature x-ray diffraction, were 480 °C, 500 °C, and 530 °C for La0.9Tb0.1NbO4+δ, La0.8Tb0.2NbO4+δ, and La0.7Tb0.3NbO4+δ, respectively. The impedance spectroscopy results suggest mixed conductivity...

The analysis of the antimony substitution influence on temperature dependence of unit cell distortion has been done. The values of spontaneous strain and Landau order parameter for three different antimony contents varied had been calculated. The phase transition occurring for antimony substituted lanthanum orthoniobate was found to be second order. The high temperature solution calorimetry method has been used to investigate...

The single phase lanthanum orthoniobate with tetragonal structure has been synthesized by the means of mechanosynthesis method. The studies have shown the crystal structure of La0.98Ca0.02NbO4 depends on the synthesis stage. The samples were predominantly in the tetragonal phase with a trace amount of the monoclinic phase. The SEM studies of morphology and microstructure have shown nanocrystallinity of the materials. The Raman...