The paper analyses the relationship between an increase of the inner diameter of tubes made of Manaurite XM cast steel and transformations occurring in their microstructure due to long-lasting operation in methane reformer. Examinations included metallographic analysis with light microscope (LM), scanning electron microscope (SEM) and microanalysis of the chemical composition of precipitates (EDX). It was indicated that there is...

Microstructure transformations occur in the Manaurite XM cast steel tubes during long-term operation in the reformer furnace were revealed and described. The rela tionship between mechanical properties, an increase of internal diameter of the tube and microstructure degradation is discussed. Static tensile test was performed on two types of samples with different shapes. It has been shown differences in the results of tests...

Purpose of this paper is to show the effect of long-term service at elevated temperatures on microstructural changes of cast steel reformer tubes made of the alloy IN-519 (24%Cr, 24%Ni, Nb). The relationship between mechanical properties and microstructure degradation is discussed. Investigations were performed on five tubes taken from ammonia reformer furnace. Tubes worked at temperature of 880C and 3,2 MPa pressure. The operation...

Degradation examinations of outer surface of low-emission steam boiler evaporator tubes are presented in the paper. Metallographic evaluation of scale morphology, its micro sites chemical composition analysis and distribution of elements on cross sections have been performed. Water-wall tubes were exposed in steam boiler for up to two years period. Common tubes made of 16Mo3 steel suffered sulphide and molten salts corrosions....

To further understand the suitability of Ni-Cr-base alloy for solid oxide fuel cell (SOFC), a commercial Ni-Cr-Fe-Mo alloy, Hastelloy X was selected and evaluated for oxidation behaviour under high temperature conditions. HastelloyX was chosen due to its unusual resistance to oxidizing, reducing and neutral atmospheres. For long term stability of metal supported fuel cell, the corrosion resistance plays a vital role and must be...