In this paper are characterized problems of high strength steel weldability in underwater wet welding conditions. Water as a welding environment intensifies action of unfavourable factors which influence susceptibility to cold cracking of welded steel joints. The susceptibility to cold cracking of S355J2G3 steel and S500M steel in wet conditions was experimentally estimated (by using Tekken test). It was concluded that the steels...
The article presents the idea of the use of Temper Bead Welding (TBW) technique to improve the weldability of high strength steel at underwater wet welding conditions. Wet welding method with the use of covered electrodes is described. This work shows results of metallographic examinations and hardness measurements of samples of S420G2+M steel with weld beads performed under water. It has been shown that Temper Bead Welding technique...
The normalized S355G10 + N steel was chosen for testing, it is used in a variety of applications including the building of offshore structures, which may require repairs in water environment. The main aim of the work was to check susceptibility to cold cracking for fillet welds – Controlled Thermal Severity (CTS) tests and butt welds – Tekken tests and in the next step evaluation of effectiveness of Temper Bead Welding (TBW) application...
seen 355 times