The aim of the present was to find more clues on the nonlinearities in impedance of oxide glasses. The first family of researched glasses has a composition of FeO-P2O5-Na2O. Oxide glasses containing iron and alkali are well known for a very low alkali ion mobility and may be considered purely polaron conducting. These glasses show no detectable nonlinearities in the impedance spectra. The second was a family of ionic conducting...

The linear and nonlinear impedance spectra of oxide glasses were measured in the frequency range of 1 mHz to 1 MHz and in the temperature range of 153K to 483K. Two groups of iron oxide glass samples were prepared, the first one containing alkaline ions and the second one without alkali. In the first group, compositions of glasses were as follows: (in %mol) 50% SiO2 , 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O,...

Nonlinear a.c. impedance measurements were performed in Cu2O-Al2O3-SiO2 glass in wide frequency range. The obtained results shows that a large nonlinearity in the impedance signal is observed at moderate electric fields of an order 1V/mm. The contents of the third harmonics reaches about 10% and strongly depends on temperature and frequency. The investigated glass exhibits mixed electronic-ionic conductivity. Electronic conduction...

The nonlinear and linear electrical properties, topography, and microstructure of bismuth-vanadate ceramics, were studied. The structurewas observed with the use of X-ray diffraction (XRD), scanning electronmicroscopy (SEM), atomic force microscopy (AFM) and confocal microscopy methods. The obtained results showed that ceramic is porous. Two phase transitionswere determinedwith the use of DSC measurements. The linear and nonlinear ac...