The Ti13Zr13Nb alloy in solid and porous form was oxidised. The constant voltage 20 V, oxidation time 0.5 and 1 h, and 1 M H3PO4 (orthophosphoric acid) with addition of HF (hydrofluoric acid) as a test solution were applied. SEM (Scanning Electron Microscope) examinations of surface, EDS (Energy Dispersive X-ray Spectroscopy) chemical analysis, nanohardness and nano-scratch tests, and corrosion potentiokinetic tests at various...

The aim of this research was to study the properties of nanohydroxyapatite (nanoHAp) and nanohydroxyapatite, doped with nanosilver (nanoHAp/nanoAg), coatings obtained by an electrophoretic deposition process. The suspensions was prepared by dispersing 0.1 g of HAp nanopowder for nanoHAp coatings and 0.1 g of nanoHAp and 0.025 g nanoAg for nanoHAp/nanoAg coatings. The deposition was carried out for 1 min at 50 V voltage followed...

Titanium and its alloys are the biomaterials most frequently used in medical engineering, especially as parts of orthopedic and dental implants. The surfaces of titanium and its alloys are usually modified to improve their biocompatibility and bioactivity, for example, in connection with the deposition of hydroxyapatite coatings. The objective of the present research was to elaborate the technology of electrophoretic deposition...

The titanium and its alloys belong at present to the most preferred and commonly applied biomaterials for load- bearing implants. The surfaces of biomaterials are subjected to modification, including the hydroxyapatite coatings deposited in order to ensure corrosion resistance and better joining between an implant and a bone through the possibility of ingrowth bone into the coating. In this paper, the morphology and properties...