Year 2023
-
Evaluation of structural and electrical properties of multicomponent spinel oxide thin films deposited via spray pyrolysis technique
PublicationThis work reports the preparation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous, and crystallised upon heat treatment at 500 ◦C. Microstructural analyses proved a homogeneous...
-
Fe-modified Mn2CuO4 spinel oxides: coatings based on abundant elements for solid oxide cell interconnects
PublicationThe current state of the art steel interconnect coating materials are based on critical raw material - Co-oxide spinels. Replacing Co-oxide spinels with alternative, abundant materials can reduce the dependence on the critical raw materials. Cobalt-free coatings with the general formula Mn2-xCuFexO4, where x = 0, 0.1, 0.3, were electrophoretically deposited on a ferritic stainless-steel support and evaluated. Prior to deposition,...
-
High-temperature Corrosion of ~ 30 Pct Porous FeCr Stainless Steels in Air: Long-Term Evaluation Up to Breakaway
PublicationIn this work, a long-term (up to 6000 hours) corrosion evaluation of three porous (~ 30 pct of initial porosity) ferritic iron-chromium alloys with different Cr contents (20, 22, and 27 wt pct of Cr) was carried out at 600 C, 700 C, 800 C, and 900 C in air. Mass gain measurements and SEM analyses revealed that at temperatures above 600 C, all alloys exhibit breakaway corrosion, whereas at 600 C, none of the alloys were heavily...
-
Impact of strontium non-stoichiometry of SrxTi0.3Fe0.7O3-δ on structural, electrical, and electrochemical properties for potential oxygen electrode of intermediate temperature solid oxide cells
PublicationThis work presents the results of a comprehensive study on the impact of the A-site non-stoichiometry of SrxTi0.3Fe0.7O3-δ (x = 0.90, 0.95, 1.00, 1.05) ceramics on their physicochemical properties. The materials were fabricated by the conventional solid-state reaction method and their structure was determined by X-ray diffractometry, X-ray photoelectron spectroscopy and electron microscopy. Their sintering and thermal expansion...
-
In situ transformation boosts the pseudocapacitance of CuNi-MOF via cooperative orientational and electronic governing
PublicationThe disordered arrangement and thereof inferior conductivity of 2D MOF sheets seriously hinder their practical application. Herein, we propose in situ transformation strategy to architect vertically oriented bimetallic CuNi-MOF as a self-supporting electrode, leading to a decuple high specific capacitance of 1262 C g-1 in comparison with the pristine Ni-MOF powder of 114 C g-1 at 2 A g-1. DFT calculations reveal that introduction...
-
Tailoring a low-energy ball milled MnCo2O4 spinel catalyst to boost oxygen evolution reaction performance
PublicationThe development of cost-efficient oxygen evolution reaction (OER) catalysts is one of the most important tasks facing modern techniques for hydrogen production. In this work, for the first time, a low-energy ball milling process of MnCo2O4 (MCO) spinel powders, with a mechanical modification time exceeding 1 day was used. After 6 days of ball-milling, the obtained overpotential of the electrocatalyst reached the value of 375 mV...
-
Tuning of eg electron occupancy of MnCo2O4 spinel for oxygen evolution reaction by partial substitution of Co by Fe at octahedral sites
PublicationTo study the effect of partial Co substitution by Fe in the B site of MnCo2O4 spinel on its physicochemical and electrochemical properties, a series of MnCo2-xFexO4 powders (x=0.125; 0.250; 0.500; 0.750; 1.000) were synthesized by means of the sol-gel method. The produced powders were characterized by powder X ray diffraction (pXRD), scanning and transmission electron microscopy (SEM & TEM) coupled with energy dispersive spectroscopy...
Year 2024
-
Enhanced Electrochemical Performance of MnCo1.5Fe0.5O4Spinel for Oxygen Evolution Reaction through Heat Treatment
PublicationMnCo1.5Fe0.5O4 spinel oxide was synthesized using the sol−gel technique, followed by heat treatment at various temperatures (400, 600, 800, and 1000 °C). The prepared materials were examined as anode electrocatalysts for watersplitting systems in alkaline environments. Solid-state characterization methods, such as powder X-ray diffraction and X-ray absorption spectroscopy (XAS), were used to analyze the materials’ crystallographic...
-
Enhanced Mechanical and Electromechanical Properties of Compositionally Complex Zirconia Zr1–x(Gd1/5Pr1/5Nd1/5Sm1/5Y1/5)xO2−δ Ceramics
PublicationCompositionally complex oxides (CCOs) or high-entropy oxides (HEOs) are new multi-element oxides with unexplored physical and functional properties. In this work, we report fluorite structure derived compositionally complex zirconia with composition Zr1- x(Gd1/5Pr1/5Nd1/5Sm1/5Y1/5)xO2-δ (x = 0.1 and 0.2) synthesized in solid-state reaction route and sintered via hot pressing at 1350 °C. We explore the evolution of these oxides'...
-
Influence of conductive carbon and MnCo2O4 on morphological and electrical properties of hydrogels for electrochemical energy conversion
PublicationIn this work, a strategy for one-stage synthesis of polymer composites based on PNIPAAm hydrogel was presented. Both conductive particles in the form of conductive carbon black (cCB) and MnCo2O4 (MCO) spinel particles were suspended in the three-dimensional structure of the hydrogel. The MCO particles in the resulting hydrogel composite acted as an electrocatalyst in the oxygen evolution reaction. Morphological studies confirmed...
-
Multilayer coatings based on cerium oxide and manganese cobaltite spinel for Crofer22APU SOC interconnects
PublicationThe current state of the art steel interconnect coating materials are based on critical raw material - Co-oxide spinels. Replacing Co-oxide spinels with alternative, abundant materials can reduce the dependence on the critical raw materials. Cobalt-free coatings with the general formula Mn2-xCuFexO4, where x = 0, 0.1, 0.3, were electrophoretically deposited on a ferritic stainless-steel support and evaluated. Prior to deposition,...
-
Ultrafast high-temperature sintering (UHS) of cerium oxide-based compound
PublicationUltrafast high-temperature sintering (UHS) is an innovative sintering technique that can densify ceramics in a few seconds, dramatically reducing the carbon footprint and firing costs. In this work, the feasibility of applying UHS in Gd-doped ceria (GDC) and GDC-Er-stabilized bismuth oxide (ESB) composite powders was investigated. At high UHS currents (22-24 A), a fully dense GDC sample with a large grain size was obtained. Nonetheless,...