Year 2014
-
Bead-on-plate welding on S235JR steel by underwater local dry chamber process
PublicationThe article presents the results of the effect of parameters of underwater local dry chamber welding on the properties of padding welds. The effect of heat input and the type of shielding gas on the structure and hardness of welds was established. the functions for estimating the maximum hardness of the heat affected zone have been also elaborated.
-
Diffusible Hydrogen Control in Flux Cored Arc Welding Process
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...
-
Weldability of S500MC Steel in Underwater Conditions
PublicationWet welding with the use of covered electrodes is one of the methods of underwater welding. This method is the oldest, the most economic and the most versatile. The main difficulties during underwater wet welding are: high cooling rates of the joint, the presence of hydrogen in the arc area and formation of hard martensitic structure in the weld. These phenomena are often accompanied by porosity of welds and large number of spatters,...
-
Wpływ warunków spawania pod wodą na skłonność stali S355G10+N do tworzenia pęknięć zimnych
PublicationPrzedstawiono wpływ parametrów spawania pod wodą na spawalność stali o podwyższonej wytrzymałości S355G10+N. Pokazano również wpływ zastosowania techniki ściegu odpuszczającego na poprawę spawalności tej stali.
Year 2013
-
DETERMINATION OF DIFFUSIBLE HYDROGEN CONTENT IN DEPOSITED METAL OF RUTILE ELECTRODES BY GLYCERIN METHOD
PublicationThe presence of diffusible hydrogen in welded joints is one of the causes of formation the welding imperfections. Improvement of weldability can be achieved by reducing the hydrogen amount in welded joints. This requires, among others, the finding of sources of hydrogen. For high hydrogen processes the commonly used method of determining the diffusible hydrogen amount is the glycerin method. This paper concerns issues related to...
-
Ocena skłonności do tworzenia się pęknięć zimnych stali podwyższonej wytrzymałości w warunkach podwodnych
PublicationReferat stanowi wprowadzenie teoretyczne do oceny skłonności do tworzenia się pęknięć zimnych stali podwyższonej wytrzymałości w warunkach podwodnych. Autor stara się wyjaśnić przyczyny powstawania pęknięć zimnych oraz metody ich zapobiegania. W artykule zawarto również opis metod spawania podwodnego oraz metod badania pęknięć zimnych. Referat stanowi wstęp teoretyczny do przyszłej rozprawy doktorskiej.
-
Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state...
-
Skłonność do tworzenia pęknięć zimnych złączy ze stali S420G2+M spawanej pod wodą metodą mokrą
PublicationPrzeniesienie procesu spawania do środowiska wodnego skutkuje przede wszystkim zwiększeniem prędkości stygnięcia złącza oraz wzrostem zawartości wodoru dyfundującego w stopiwie. Środowisko wodne powoduje istotne pogorszenie spawalności stali jednak zastosowanie odpowiedniej technologii spawania pozwala na uzyskanie złączy o właściwościach zbliżonych do wykonywanych na powietrzu. W pracy oceniono przydatność drobnoziarnistej stali...
-
Wpływ warunków spawania drutem proszkowym samoosłonowym na ilość wodoru dyfundującego
PublicationBadania przeprowadzone przy zastosowaniu planowania badań (wg dwupoziomowego planu Placketta-Burmana) pozwoliły na określenie istotności wpływu pięciu czynników na zawartość wodoru dyfundującego w stopiwie uzyskanym podczas spawania mokrego drutem proszkowym samoosłonowym (114): długości wolnego wylotu, natężenia prądu spawania, napięcia łuku, prędkości spawania i zasolenia wody. Opracowano równanie umożliwiające prognozowanie...