Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide Bi2O3+Gd2O3 structures
Open Research DataExcel (*.xlsx) and Csv (*.csv) files containing raw mechanical (compressive strength) data of cement pastes after 1, 2, 7 and 28 days of curing
-
Rheological properties of cement pastes containing pristine Bi2O3-Gd2O3 and silica coated Bi2O3-Gd2O3 core-shell structures
Open Research DataRheological data of cement pastes containing Bi2O3/Gd2O3 particles using MCR 72 (Anton Paar) stress-imposed rheometer, equipped with vane geometry.
-
Mechanical properties of concrete mixes M0-M100 concrete mixes
Open Research DataDataset of hardneded properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.Excel file consists results of:
-
Fresh properties of concrete mixes M0-M100 concrete mixes
Open Research DataDataset of fresh properties of concretes containing different amount of magnetite aggregate (M0-M100) mixes.*. ODS - open-source spreadsheet file file consists results of:
-
Green strength (buildability performance) of concretes containing magnetite aggregate (M0-M100) mixes
Open Research DataRaw data for determination of buildability (green strength) properties of concrete mixes determined by squeezing test using QuantumX MX840B with CATMAN-EASY software, determined after 15, 30, 45 and 60 minutes. Values present force and two displacement measurements by LVDT.Additionally, an Origin (*.opju) file with processed data presenting stress-strain...
-
Adiabatic calorimetry results for fresh concrete mixes M0 and M100
Open Research DataAdiabatic calorimetry results for fresh 3D printed concrete mixes (M0 and M100) determined using Controls S.p.A., Italy calorimeter
-
Open porosity and oven-dry density of concretes containing magnetite aggregate (M0-M100) mixes
Open Research DataRaw data for determination of open porosity and oven-dry densities of concretes containing different amount of magnetite aggregate (M0-M100) mixes. Sample designation is related to the publication associated with dataset.
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Open Research DataExcel file containing raw mechanical (compressive strength) data of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.