The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Description
The ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA) in a molar ratio equal to 2:1 until a white slurry was obtained. The water-based solution was then added to a titanium precursor mixture and stirred at 80C until fully dissolved. After this, the solution was heated to 150C and condensed until gel was obtained. Next, the gel was transferred into an alumina crucible and calcined for 1 h at 400C, then for 1 h at 600C and finally at 1200C for 12 h under an air atmosphere.
Dataset file
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} where a single part of the file is 512 MB in size.Example script for calculation:
https://github.com/antespi/s3md5
File details
- License:
-
open in new tab
CC BYAttribution - File embargo:
- 2026-04-30
- Raw data:
- Data contained in dataset was not processed.
Details
- Year of publication:
- 2024
- Verification date:
- 2024-03-11
- Dataset language:
- English
- Fields of science:
-
- materials engineering (Engineering and Technology)
- DOI:
- DOI ID 10.34808/fe9m-yz29 open in new tab
- Funding:
- Verified by:
- Gdańsk University of Technology
Keywords
Cite as
Authors
seen 80 times