Abstract

Purpose: The aim of this paper is to compare optical properties of 4-(1,1,1,3,3,3-hexafluoro-2(-4(-3(4-(5-(4-m-tolyoxy)phenyl)-1,3,4-oxadiazol-2-yl)phenoxy)phenylcarbomyl)phenyl)propan2-yl)-N-methylbenzamide(Oxad 6F-D) and 4-(1,1,1,3,3,3-hexafluoro-2(-4-(4-(4-(5-(4-(p-tolyoxy)phenyl)-1,3,4-oxadiazol-2-yl)phenoxycarbaomyl)phenyl)propan-2-yl)-N-methylbenzamide (Oxad 6F-E).Design/methodology/approach: The Oxad 6F polymer thin films were deposited onto glass and KBr substratesby spin–coating method under different technological conditions.Findings: The spinning rate V and solution concentration C influenced optical properties of Oxad 6F-D andOxad 6F-E thin films. The goal of this paper is to show differences in properties of these polymers.Research limitations/implications: The electrical and luminescent properties of Oxad 6F polymers will becarried out in the nearest time. The different properties of these polymers are caused by benzene position in thepolymer chain, two aromatic rings are in meta-position in Oxad 6F-D and all benzene rings are in para-positionsin Oxad 6F-E.Practical implications: Thin films of Oxad 6F-D and Oxad 6F-E are good potential material for applicationsin polymer optoelectronic devices.Originality/value: The aim of this paper is to describe the optical properties of Oxad 6F polymers preparedunder different technological conditions
(PDF) Comparing of optical properties and morphology of polyoxadiazoles with CF3 groups. Available from: https://www.researchgate.net/publication/44567557_Comparing_of_optical_properties_and_morphology_of_polyoxadiazoles_with_CF3_groups [accessed Oct 29 2024].

Author (1)