Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load

Wojciech Macek; Dariusz Rozumek; Sebastian Faszynka; Ricardo Branco; Shun-Peng Zhu; Reza Masoudi Nejad

doi:10.1016/j.engfailanal.2023.107285

Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load

Abstract

In this study, fatigue fracture surfaces of aluminium alloy 2017-T4 notched specimens were investigated under cyclic bending to find an alternative failure loading index.. The surface topographies were measured on the entire fracture area with an optical profilometer for different loading conditions. Fatigue crack initiation life Ni and total fatigue life Nf were examined using standard surface topography parameters (such as, root mean square height Sq, arithmetical mean height Sa, maximum height Sz) and non-standard surface topography parameters (such as, fractal dimension Df). Fatigue life assessment was successfully performed by combining both fracture surface topography and stress state features. The results show that the fracture plane geometry, expressed by the fractographic-fractal dimension, can facilitate the estimation of post-failure loading history.

Citations

1 7

CrossRef
0

Web of Science
1 7

Scopus

Authors (6)

Cite as

Full text

download paper

downloaded 46 times

Publication version: Accepted or Published Version
DOI:: Digital Object Identifier (open in new tab) 10.1016/j.engfailanal.2023.107285
License: open in new tab

full content of the article see on external site open in new tab

Keywords

Details

Category:

Articles

Type:

artykuły w czasopismach

Published in:

ENGINEERING FAILURE ANALYSIS no. 149,
ISSN: 1350-6307

Language:

English

Publication year:

2023

Bibliographic description:

Macek W., Rozumek D., Faszynka S., Branco R., Zhu S., Masoudi Nejad R.: Fractographic-fractal dimension correlation with crack initiation and fatigue life for notched aluminium alloys under bending load// ENGINEERING FAILURE ANALYSIS -Vol. 149, (2023), s.107285-

DOI: