Morphology of the sol-gel derived LTO:Cu films
Open Research DataMorphology of the lithium titanate doped by Cu thin films were investigated by SEM microscope. Films were deposited by spin-coater from sol-gel derived sol. SEM images showed a high porous structure, tipaciall for sol-gel based films. For measurements samples with a various content of Cu were selected.
-
Sol-gel derived TeO2:RE powders
Open Research DataTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
Optical measurements of LTO:Cu sol-gel derived thin films
Open Research DataLithium titanate doped by copper thin films were manufactured by chemical, sol-gel method. Flms were deposited on a Corning glass substrated by spin coater. To calculated optical band gap and other optcal parameters, UV-VIS spectroscopy measurements were performed. For measurements selected samples with various content of Cu.
-
Raman spectroscopy analysis of synthesized sol-gel silica coatings
Open Research DataThese data contains Raman spectra of silica coatings synthesized using sol-gel method A and B, which were described with publication associated with this dataset. Raman scattering was measured with a Renishaw microRaman spectrometer (830 nm).
-
Optical measurements of lithium titanate sol-gel derived thin films
Open Research DataNanocrystalline thin films with 800 nm thickness were prepared by sol–gel method. To examine the influence of the annealing time on as-prepared films crystallization, the coatings were heated at 550 °C for 10, 20 and 80 h. On the basis of transmission characteristic optical properties were calculated. It was found that transmission through the thin...
-
Sol-gel derived lithium titanate powders measured by XPS method
Open Research DataFor sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate and copper nitrate were dissolved...
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Open Research DataLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
Luminescence properties of TeOx-Dy gels
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Luminescence properties of TeOx-Tb gels
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb gel. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The sol was...
-
Luminescence properties of TeOx gels
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
SEM analysis of the TiO2 layers deposited on a FTO substrates
Open Research DataTitanium dioxide layers were deposited on a FTO conducting glass by sol-gel method. For sol gel synthesis butoxy titanium and ethanol were used as a reagents. Samples were sintered in a furnace at temperature of 600 deg. SEM measurements were performed by FEI Quanta FEG250 microscope. SEM images of a cross-section of samples exhibit a porous structures...
-
XPS study of the NH4-VOx powders
Open Research DataVanadium pentoxide samples were prepared by sol-gel method. The starting solution was prepared by mixing vanadium (V) oxytripropoxide (Aldrich) in an anhydrous ethanol as solvent and acetylacetone. By drying the sol at 323 K for 48 h, it transforms via gel into a xerogel powder. Next, the precursor powder was pressed into the disk-shaped pellets. Samples...
-
XPS study of the lithium titanate doped by copper
Open Research DataLithium titanate doped by copper was measured by X-ray photoemission spectroscopy. For sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal...
-
Analysis of the electrical parameters of the LTO thin films
Open Research DataLithium titanate thin films were derived by sol-gel technique. Films with thickness ca. 800 nm were annealed for various time, in a range of 10h-80h at 550 deg. Electrical conductivity in a wide range of temperature was measured.
-
Luminescence properties of TeOx thin films annealing under an oxidizing atmosphere
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
Luminescence properties of TeOx-Eu gels
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu gels. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The sol...
-
Luminescence properties of TeOx-Eu thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Tb thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Dy thin films
Open Research DataThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
The AFM micrographs of vanadium oxides thin films obtained at 800°C
Open Research DataThe DataSet contains the atomic force microscope images of the surface of vanadium oxide thin films. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The sol was deposited on a silicon substrate and vanadium thin films were obtained by annealing as-prepared films at...