Diffusible Hydrogen Control in Flux Cored Arc Welding Process
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...
-
Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state...
-
Microstructure and Mechanical Properties of Combined GTAW and SMAW Dissimilar Welded Joints between Inconel 718 and 304L Austenitic Stainless Steel
PublicationA dissimilar welded joint of Inconel 718 and 304L austenitic stainless steel was prepared using a combined procedure with the gas tungsten arc welding and shielded metal arc welding processes by employing the Ni-based fillers: ERNiCr-3 and ENiCrFe-3. The welded joints were investigated for metallographic testing and mechanical properties, and a relationship was established between the microstructure and the resultant mechanical...
-
Underwater Local Cavity Welding of S460N Steel
PublicationIn this paper, a comparison of the mechanical properties of high-strength low-alloy S460Nsteel welded joints is presented. The welded joints were made by the gas metal arc welding (GMAW)process in the air environment and water, by the local cavity welding method. Welded joints were testedfollowing the EN ISO 15614-1:2017 standard. After welding, the non-destructive—visual, penetrant,radiographic, and ultrasonic (phased array) tests...
-
Wire Arc Additive Manufactured Mild Steel and Austenitic Stainless Steel Components: Microstructure, Mechanical Properties and Residual Stresses
PublicationWire arc additive manufacturing (WAAM) is an additive manufacturing process based on the arc welding process in which wire is melted by an electric arc and deposited layer by layer. Due to the cost and rate benefits over powder-based additive manufacturing technologies and other alternative heat sources such as laser and electron beams, the process is currently receiving much attention in the industrial production sector. The gas...
-
Determination of t8/5 cooling times for underwater local dry welding of steel
PublicationKnowledge of thermal history is the basic condition for studying the structure - properties of welded joints. The determinant of thermal history is the thermal cycle, whose in-situ measurements are still a big challenge. Water as the welding environment complicates this issue even more. The article presents a method to determine an equation for calculating t8/5 cooling times for underwater gas metal arc welding of unalloyed steels...
-
Diffusible hydrogen management in underwater wet self-shielded flux cored arc welding
PublicationThis article reports the effect of underwater wet welding parameters and conditions on the diffusible hydrogen content in deposited metal for welding with a self-shielded flux cored wire. The diffusible hydrogen content in deposited metal was determined using the glycerin method according to the Plackett-Burman design determining the significance of the effect of the stick out length, welding current, arc voltage, travel speed...
-
Metallurgical characterization and high-temperature tensile failure of Inconel 617 alloy welded by GTAW and SMAW—a comparative study
PublicationTwo types of the weld joint of Inconel 617 alloy were produced using gas tungsten arc welding (GTAW) and shielded metal arc welding (SMAW) processes with ERNiCrCoMo-1 filler metal and ENiCrCoMo-1 electrode, respectively. The weld metal showed the segregation of the principle alloying elements like Mo and Cr along the inter-dendritic spaces, triggering the formation of secondary phases. The microstructure characterization of the...
-
Effect of underwater local cavity welding method conditions on diffusible hydrogen content in deposited metal
PublicationOne of the methods with great potential for applications in underwater repairs is local cavity welding. In local cavity method, cooling conditions and diffusible hydrogen amount in weld metal are nearly the same as those existed during welding in the air. This paper presents the results of literature survey and preliminary tests of the effect of local cavity welding conditions on diffusible hydrogen amount in a deposited metal....
-
Study on Microstructural Characterization, Mechanical Properties and Residual Stress of GTAW Dissimilar Joints of P91 and P22 Steels
PublicationThis article deals with the dissimilar joining of two different grade Cr-Mo steel (2.25Cr-1Mo: P22 and modified 9Cr-1Mo: P91) for power plant application. The dissimilar butt-welded joint was produced for conventional V groove design by using the gas tungsten arc welding (GTAW) process with the application of an ERNiCrMo-3 Ni-based super alloy filler. A microstructure characterization was performed to measure the inhomogeneity...
-
The Effect of Welding Conditions on Diffusible Hydrogen Content in Deposited Metal
PublicationThe article presents the results of a literature survey and preliminary tests which set out effects of welding conditions on the amount of diffusible hydrogen in deposited metal. Experiments were conducted by using rutile coated electrodes which generate high contents of diffusible hydrogen in deposited metal. The amount of diffusible hydrogen was determined by a glycerin test.Eleven factors were considered: the electrode angle,...
-
Effect of underwater wet welding conditions on the diffusible hydrogen content in deposited metal
PublicationIn the study mercury displacement method was used for determination of diffusible hydrogen amount in deposited metal obtained during underwater wet welding with covered electrodes in laboratory conditions according to a two-level full factorial design for three factors. The factors and their levels were chosen among conditions and parameters of welding in accordance with the results of own preliminary studies. A statistical analysis...
-
Effect of Arc Strikes on High Strength Low Alloy Steels Welded by SMAW
PublicationWet welding with covered electrodes (Shielded Metal Arc Welding – SMAW) is the most commonly used method of carrying out welding repair works in a water environment. Limited visibility and the inability to move freely under water result in an increased risk of formation of welding imperfections such as lack of fusion, lack of penetration and arc strikes. The work focused on changes in the properties and structure of steel subjected...
-
The Effect of Welding Conditions on Mechanical Properties of Superduplex Stainless Steel Welded Joints
PublicationThe tests results of superduplex stainless steel welded joints made with a different heat input, using automatic submerged arc welding (SAW) and semi-automatic flux-cored arc welding (FCAW) have been presented. Metallographic examinations, the measurements of the ferrite content, the width of the heat affected zone (HAZ) and the hardness of the welds in characteristic areas have been performed. Significant differences in the amount of...
-
Effect of water salinity on properties of multipass underwater wet manual metal arc welded joints
PublicationThe weldability of steel under the water is limited due to the influence of the environment. Water causes limited visibility, presence of the residual stresses, increasing the cooling rate, and increasing the diffusible hydrogen content in deposited metal, leading to the formation of brittle microstructures in heat-affected zone (HAZ). The paper presents the results of mechanical properties testing of S420G2+M steel welded joints...
-
Assessment of hydrogenation of deposited metal of P 62 MR covered electrodes
PublicationThe determination of diffusible hydrogen content in deposited metal of P 62 MR covered electrodes for manual metal arc welding by mercury method was carried out. The test results indicate that covered electrodes 62 P MR grade generate a mean of 4.02 ml/100g of diffusible hydrogen in deposited metal, which is consistent with H5 class.
-
Effect of shielded electrode wet welding conditions on diffusible hydrogen content in deposited metal
PublicationWet welding is the most popular method of joining in water enviroment. During underwater welding, the weldability of steel is limited by the higher cooling rates and hydrogen content in weld metal. Article presents results of preliminary tests on the effects of wet welding conditions on diffusible hydrogen amount. Seven parameters were optimized using a Plackett-Burman plan to get the most relevant variables. These parameters were:...
-
Exploring the trends in flux-cored arc welding: scientometric analysis approach
PublicationFlux-cored arc welding (FCAW) is a universal group of welding methods in terms of the scope of application and automation possibilities, the share of which in various industries in many countries is still increasing. The paper presents the results of bibliographic analyses (scientometric analysis with the use of VOSviewer, Bibliometrix and CitNetExplorer tools) of a data set of 993 publications indexed in the Web of Science database...
-
P92 steel and inconel 617 alloy welds joint produced using ERNiCr-3 filler with GTAW process: Solidification mechanism, microstructure, mechanical properties and residual stresses
PublicationThe objective of the current study was to analyse the microstructure, mechanical characteristics, and residual stresses of a dissimilar welded joint (DWJ) made of P92 steel and the Inconel alloy 617 (IN617) using the gas tungsten arc welding (GTAW) method. The ERNiCr-3 filler was selected to produce the conventional V groove (VG) and narrow V groove (NVG) butt joint. The filler deficient zones in the weldments, such as the filler...
-
Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
PublicationThe electrochemical behavior of the weld metal, heat-affected zone (HAZ), and base material of super duplex stainless steel (SDSS) welded joints, made with the application of flux-cored arc welding (FCAW) and submerged arc welding (SAW), were investigated with the use of metallographic examinations (optical microscopy and scanning electron microscopy), potentiodynamic polarization measurements and total hydrogen content determination...