Steel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life, the pipeline must be reliable. Loss of structural integrity can result in environmental disaster and high economic costs. For these reasons, the material undergoes very detailed quality control. As part of this, the required mechanical properties are checked.
Steel plates made of API 5L X65 steel, 19 mm thick, were tested. The research included tensile test and CTOD (Crack Tip Opening Displacement) test. The mechanical properties of the test material were checked along and across the rolling direction. Subsequently named as XY and YX directions. For tensile test, two operating temperatures were considered - room temperature +20°C and reduced to -10°C. It is well known that fracture toughness decreases with temperature decrease. It is the reason why CTOD test was carried out only in temperature -10°C – the worst case for planned steel application.
Presented dataset contains fracture documentation of speciemens tested along rolling direction
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BY-NCUżycie niekomercyjne
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-04-29
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria mechaniczna (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/arjq-5c45 otwiera się w nowej karcie
- Seria:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Cytuj jako
Autorzy
wyświetlono 135 razy