CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21

Opis

Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN  over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. 
Overall test time till coating penetration 9 min. The test was run in an intermittent mode with coating's condition examination at 3 min intervals.
Secimen numbers: A25 (top, rotating), B21 (bottom, non-rotating).
Data format: Matlab. Data condition: processed.
Data vectors in *.mat file:
time_zbior - overall test's running time,
U_zbior - overall friction coefficient .

Plik z danymi badawczymi

wsp_tar_wykres_A25B21_9min.mat
53.1 MB, S3 ETag f6a98a333242489e956f44177932c119-1, pobrań: 51
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by-nc 4.0 otwiera się w nowej karcie
CC BY-NC
Użycie niekomercyjne

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-06-21
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria mechaniczna (Dziedzina nauk inżynieryjno-technicznych)
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/hsr2-nd25 otwiera się w nowej karcie
Seria:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 95 razy