CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21

Opis

Wear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN  over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. 
Overall test time till coating penetration 25 min. The test was run in an intermittent mode with coating's condition examination at 3 min intervals with incremental increase of time interval to 5, 10 and 20 min.
Secimen numbers: B21 (top, rotating), A21 (bottom, non-rotating).
Data format: Matlab. Data condition: processed.
Data vectors in *.mat file:
time_zbior - overall test's running time,
U_zbior - overall friction coefficient .

Plik z danymi badawczymi

wsp_tar_wykres_B21A21_25min.mat
68.8 MB, S3 ETag ef20037dd4871a893ef55970d849fea5-1, pobrań: 58
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by-nc 4.0 otwiera się w nowej karcie
CC BY-NC
Użycie niekomercyjne

Informacje szczegółowe

Rok publikacji:
2021
Data zatwierdzenia:
2021-06-21
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria mechaniczna (Dziedzina nauk inżynieryjno-technicznych)
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/8z33-0n74 otwiera się w nowej karcie
Seria:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

wyświetlono 110 razy