Opis
The linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to 673K and formed into small circular-shaped pellets (about 1,5 mm thick and 20 mm in diameter). Next glasses were annealing at the 673K and cooling with furnance. After a polishing, golden electrodes were evaporated at both sides of preheated samples in vacuum, for the electrical conductivity measurements. The linear and nonlinear impedance spectra were measured in the frequency range of 1 mHz to 1 MHz and in the temperature range of 153K to 483K by Concept 40 broadband dielectric spectrometer. Detailed information you can find in: http://dx.doi.org/10.1016/j.ssi.2013.10.008
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2014
- Data zatwierdzenia:
- 2021-05-05
- Data wytworzenia:
- 2011
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/eczn-q298 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
- publikacja Electronic conductivity in the SiO2–PbO–Fe2O3 glass containing magnetic nanostructures
- dane badawcze Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Cytuj jako
Autorzy
wyświetlono 107 razy