Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region

Opis

The nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.

The polycrystalline Bi2VO5.5 ceramic was synthesised via a conventional solid state reaction route. The stoichiometric mixture of initial powders of Bi2O3 and V2O5 were ball-milled in pure acetone for 6 h. The milling was performed in steps of 1 h with rest intervals of 10 min. The mixture was initially heated up to 770 K and then to 1020 K in air. It was kept at this temperature for 24 h and grinded next. The calcined powder was mixed with a small amount of ethyl alcohol binder and cold-pressed into pellets (12 mm in diameter and 2–3 mmin thickness) under a compacting pressure of 26 kNcm−2. The obtained pellets were sintered at 1070 K for 24 h with heating and cooling rates of 50 Kh−1. The sample thickness was 2.91 mm.

For the electrical measurements gold electrodes were evaporated at the preheated samples. Impedance measurements were carried out in the temperature range from 473 K to 913 K, frequency of : 0.01, 0.1, 1, 10, 100 and 1000 Hz, with the ac voltage ranging from 0.01 to 3 Vrms with Concept 40 broadband dielectric spectrometer. The higher harmonic components (harmonic 1 and 2) were measured. Measurements were conducted during heating and cooling. Here the impedance for harmonic components was defined as the ratio of the voltage base wave to the n-th harmonic current component: Zn∗= U0∗/In∗, where Zn⁎ including the base wave generally depend on the sample voltage U1⁎ base wave amplitude. From Zn⁎ allother independent variables are calculated. The dependence of current density on the cosinusoidal electric field E(t)= E0cos(ωt) leads to the following expression:

j´ = σ´0hE0 cos (ωt) + σ´1hE0 cos (2ωt) + σ´2hE0 cos (3ωt) + …
Where σ´0h denotes base conductivity, while σ´1h, σ´2h etc. are higher harmonics conductivity. The admittivity for harmonic components with n ≥1, is calculated from relation σ⁎n = i2πfε0ε⁎n.

Plik z danymi badawczymi

114.zip

2.2 MB, S3 ETag b7100e54df5f63e25499e41157026842-1, pobrań: 53

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2015

Data zatwierdzenia:

2021-07-14

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/fchq-ax94

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

Autorzy

wyświetlono 112 razy

Wyszukiwarka