Scanning electron microscopy studies of the weld decay on SS 304 of water supply pipeline

Opis

This dataset contains micrographs made with scanning electron microscope (SEM) Hitachi S-3400N, of the weld decay for water supply system pipelines made of AISI 304 stainless steel. Within the dataset one can see the different corrosion mechanisms. The micrographs were made after the Strauss test (excluding pictures labeled as pits_in_HAZ, done without pre-treatment) without any further surface treatment. The weld decay is often occurring reason for corrosion failure due to pitting and intergranular attack as a result of sensitization during the welding process. Thus, different areas are shown, within weld, heat affected zone (HAZ) and base material. More studies related to these data can be found in Construction and Building Materials manuscript, 10.1016/j.conbuildmat.2014.04.058

Plik z danymi badawczymi

Weld_decay.zip

72.9 MB, S3 ETag 10f691b9e4bf4032cb64c8c78a38b9dd-1, pobrań: 75

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY-NC-SA

Użycie niekomercyjne - Na tych samych warunkach
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2020

Data zatwierdzenia:

2020-12-17

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
nauki chemiczne (Dziedzina nauk ścisłych i przyrodniczych)

DOI:

10.34808/1gkc-6z72

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Determination of causes of accelerated local corrosion of austenitic steels in water supply systems

Cytuj jako

Autorzy

wyświetlono 161 razy

Wyszukiwarka