Wyszukiwarka
Opis
The dataset includes the electrical properties mesurements of SOFC with Ce0.9Co0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding at 750oC. The layers were sintered at 1100oC.
'Such prepared fuel cells were mounted in a measurement rig. They were heated up to 800 °C with argon delivered to the anode side and then, in order to reduce nickel oxide, humidified hydrogen (3% H2O) was supplied at 800 °C for 30 min and further at 750 °C for 20 h. After this time the hydrogen was replaced by wet synthetic biogas (3% H2O) consisting of methane and carbon dioxide mixed at a volume ratio of 60/40. The total flow rate of the gas mixture was 30 cm3 min−1. Two types of electrical measurements were collected during fuel cell operation in biogas: a current density versus voltage and a current density versus time at 0.65 V for the time 120 h at 750 °C.' (10.1016/j.ssi.2018.12.007Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie))
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BY-NCUżycie niekomercyjne - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-06-10
- Data wytworzenia:
- 2018
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/w46p-ww02 otwiera się w nowej karcie
- Finansowanie:
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Powiązane zasoby
Cytuj jako
Autorzy
wyświetlono 117 razy