The luminescence study of Bi-doped Cs2AgInCl6 double perovskite.

Opis

Here, we report a halide precursor acid precipitation method to synthesize Cs₂AgIn_1−xBi_xCl₆ (x = 0, 0.02, 0.04, 0.08, 0.16, 0.32, 0.64, and 1) microcrystals. Cs₂AgInCl₆ and Bi derivative double perovskites show broadband white light emission via self-trapped excitons (STEs) and have achieved the highest internal quantum efficiency of up to 52.4% at x = 0.08. Synchrotron X-ray diffraction confirmed the linear increase of lattice parameters and cell volume with Bi³⁺ substitution at In³⁺ sites. Absorbance, photocurrent excitation, and photoluminescence excitation spectra are used to observe possible transitions from the valence to the conduction band or free exciton (FE) states as well as transitions within local Bi³⁺ states. The broadband photoluminescence is quenched via a single nonradiative process with an activation energy ΔE = 1490 cm⁻¹ for Cs₂AgIn_0.92Bi_0.08Cl₆. Under normal conditions, we observed STE emission, but applying external pressure alters the electronic structure such that at elevated pressure, the only emission via the FE state is observed. We anticipate that structure, temperature, and pressure-dependent photoluminescence studies will help the future use of a single-source lead-free double perovskite for white light-emitting diode applications.

In that dataset, the raw data of RT excitation, emission, absorption, and photocurrent excitation spectra, decay profiles, and temperature- and pressure- dependence of photoluminescence excitation, photoluminescence, and decay profiles are provided.

Plik z danymi badawczymi

Cs2AgInCl6_Bi.rar

11.7 MB, S3 ETag cc6d54afeae94c50f8aa615f1474e600-1, pobrań: 69

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2022

Data zatwierdzenia:

2022-03-04

Język danych badawczych:

angielski

Dyscypliny:

nauki fizyczne (Dziedzina nauk ścisłych i przyrodniczych)

DOI:

10.34808/wc17-7f96

Weryfikacja:

Brak weryfikacji

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 137 razy

Wyszukiwarka