The morphology of vanadate glasses containing BaTiO3

Opis

The morphology of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass plate and pressed by another plate. An Olympus LEXT OLS4000 confocal scanning laser microscope (CSLM, Olympus Life Science, Hambur, Germany ) was used to examine the morphology of as-quenched surfaces and polished surfaces of samples. 3D color images were obtained using a 405 nm laser and photomultiplier detector with the maximum obtained optical magnification of 2160x.

Detailed information can be found in: http://dx.doi.org/10.1016/j.jnoncrysol.2014.01.008

Plik z danymi badawczymi

set15.zip

224.1 MB, S3 ETag 5bf226e40ee530b0528604952308bd16-1, pobrań: 58

Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

pobierz

Informacje szczegółowe o pliku

Licencja:: otwiera się w nowej karcie

CC BY

Uznanie autorstwa
Dane surowe:: Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:

2014

Data zatwierdzenia:

2021-05-23

Data wytworzenia:

2013

Język danych badawczych:

angielski

Dyscypliny:

inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)

DOI:

10.34808/axjf-kn74

Weryfikacja:

Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

publikacja Nanostructure and dielectric behavior of vanadate glasses containing BaTiO3

Cytuj jako

Autorzy

wyświetlono 115 razy

Wyszukiwarka