The structure of 50(2Bi2O3-V2O5)-50SrB4O7 measured with X-ray diffraction method during heating - Open Research Data - MOST Wiedzy

Wyszukiwarka

The structure of 50(2Bi2O3-V2O5)-50SrB4O7 measured with X-ray diffraction method during heating

Opis

The structure changes of 50(2Bi2O3-V2O5)-50SrB4O7 glass occurred during increase in temperature was measured by XRD. 

The polycrystalline strontium–borate, SrB4O7 was synthesized via a solid state reaction route that involved heating stoichiometric mixtures of analytical grade SrCO3 and H3BO3 at 1073 K for 12 hours. Next, sample of a composition of 50(2Bi2O3-V2O5)-50SrB4O7 (in %mol) were prepared from reagent-grade Bi2O3, V2O5 and preprepared SrB4O7. Samples of glass were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at 1373 K for 2 hours. The melt was poured onto a preheated (573 K) brass plate and pressed by another plate to obtain flat circular disks of 1–2 mm thickness and 20–30 mm in diameter.

The presence of crystalline phases and their phase composition were studied using an X-ray diffraction (XRD) method using a Philips X'Pert Pro MPD system with CuKα radiation. The XRD measurements were conducted on powdered as-quenched sample at different temperatures ranges from 35 degC till 540 degC, in heating mode.

Plik z danymi badawczymi

set29.zip
192.5 kB, S3 ETag 2cb1437482a94090121bd2d4d14cc24a-1, pobrań: 58
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
pobierz plik set29.zip

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.

Informacje szczegółowe

Rok publikacji:
2015
Data zatwierdzenia:
2021-05-26
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/t45n-2e17 otwiera się w nowej karcie
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Powiązane zasoby

Cytuj jako

wyświetlono 130 razy