The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen - Open Research Data - MOST Wiedzy

Twoje konto

zaloguj

Wyszukiwarka

The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen

Opis

The (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground in an agate mortar, pressed back into pellets, heated in an oven at 1400 °C for 12 hours and cooled to room temperature at a rate of 5 °C/min. The XRD analysis allowed for determining the phase composition of powders after reduction at 1100 deg.C in hydrogen. 

Plik z danymi badawczymi

XRD red 1100.rar
39.8 kB, S3 ETag 732b21086a3d49e89f002d49fc1c3e85-1, pobrań: 7
Hash pliku liczony jest ze wzoru
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MB

Przykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5

Informacje szczegółowe o pliku

Licencja:
Creative Commons: by 4.0 otwiera się w nowej karcie
CC BY
Uznanie autorstwa
Embargo na plik:
2026-04-18
Dane surowe:
Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
Oprogramowanie:
High Score

Informacje szczegółowe

Rok publikacji:
2023
Data zatwierdzenia:
2023-03-07
Data wytworzenia:
2022
Język danych badawczych:
angielski
Dyscypliny:
  • inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
DOI:
Identyfikator DOI 10.34808/agzw-6215 otwiera się w nowej karcie
Finansowanie:
Seria:
Weryfikacja:
Politechnika Gdańska

Słowa kluczowe

Cytuj jako

Autorzy

wyświetlono 102 razy