Niobium doped strontium vanadate based perovskite SrV1-xNbxO3-δ materials were prepared via conventional solid state reaction (SSR) method. For comparison, different samples with a various amount of niobium dopant in the structure were synthesized; x = 0; 0,2; 0,5; 0,8 and 1. Samples were sintered by two-steps: first under a pure hydrogen (purity >99.999%) atmosphere at 600 °C for 10 h and at 800 °C for 10 h; and the second stage was at 1200 °C for 10 h in pure H2 atmosphere. The composition and valence states of elements in Nb-V-Sr-O ceramics were measurements. For investigatons, the XPS method were used. Analysis exhibit a mixed valence state of transition metals. Additionaly composition was calculated. It was in a line with stoichiometry of starting precursors in a solid state reaction.
Plik z danymi badawczymi
hexmd5(md5(part1)+md5(part2)+...)-{parts_count} gdzie pojedyncza część pliku jest wielkości 512 MBPrzykładowy skrypt do wyliczenia:
https://github.com/antespi/s3md5
Informacje szczegółowe o pliku
- Licencja:
-
otwiera się w nowej karcie
CC BYUznanie autorstwa - Dane surowe:
- Dane zawarte w datasecie nie zostały w żaden sposób przetworzone.
- Oprogramowanie:
- origin
Informacje szczegółowe
- Rok publikacji:
- 2021
- Data zatwierdzenia:
- 2021-06-25
- Data wytworzenia:
- 2016
- Język danych badawczych:
- angielski
- Dyscypliny:
-
- inżynieria materiałowa (Dziedzina nauk inżynieryjno-technicznych)
- DOI:
- Identyfikator DOI 10.34808/8087-b328 otwiera się w nowej karcie
- Weryfikacja:
- Politechnika Gdańska
Słowa kluczowe
Cytuj jako
Autorzy
wyświetlono 109 razy