Abstrakt
Ag/Pt-modified TiO2nanocomposites were synthesized using the sol–gel method. The effect of metal typeand amount as well as synthesis route on the photocatalytic activity in reaction of toluene removal, usedas a model volatile organic compound, was investigated. Toluene, at the concentration of about 200 ppm,was irradiated over modified TiO2using light-emitting diodes (LEDs, max= 415 nm). The results showedthat toluene could be mostly removed from the air after 20 min of irradiation over TiO2modified withAg/Pt bimetallic nanoparticles. The efficiency of toluene degradation in four subsequent cycles decreasedfrom 99 to 53%, but it could be re-established by thermal treating of the sample. The photocatalyst show-ing the highest degradation rate consisted of large crystallites of Ag with a diameter of about 15–30 nmwith fine Pt nanoparticles ranging from 0.8 to 2.0 nm surrounding TiO2layer.
Cytowania
-
5 5
CrossRef
-
0
Web of Science
-
6 1
Scopus
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
CATALYSIS TODAY
nr 230,
strony 104 - 111,
ISSN: 0920-5861 - Język:
- angielski
- Rok wydania:
- 2014
- Opis bibliograficzny:
- Zielińska-Jurek A., Zaleska-Medynska A.: Ag/Pt-modified TiO2 nanoparticles for toluene photooxidation in the gas phase// CATALYSIS TODAY. -Vol. 230, (2014), s.104-111
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.cattod.2013.11.044
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 151 razy