An attempt to mechanistically explain the viscoelastic behavior of transparent epoxy/starch-modified ZnO nanocomposite coatings

Abstrakt

The effects of bare and starch-modified ZnO (ZnO-St) nanoparticles on viscoelastic and mechanical properties are studied by dynamic mechanical and tensile analyses. Transparent epoxy-based nanocomposite films are prepared by incorporating bare or starch-modified ZnO particles into the epoxy matrix. The results demonstrated that ZnO particles hindered the curing reactions and hence the final properties of the cured epoxy. As a result, glass-transition temperature (Tg) and crosslinking density demoted. However, starch as a surface modifier compensated for the undesired effects of ZnO in a way that by enhancing the curing reactions through autocatalytic mechanism, Tg and crosslinking density increased. The storage moduli for epoxy, epoxy/ZnO and epoxy/ZnO-St are accordingly as 13.84, 3.95 and 19.54 MPa. Therefore, the molecular weight between the entanglements is calculated as 0.2878, 1.0089 and 0.2039 in the same order. Moreover, considering the peaks of the tanδ diagrams, Tgs for epoxy, epoxy/ZnO and epoxy/ZnO-St are obtained as 95.95, 100.16 and 101.24 °C, respectively. Comparing epoxy/ZnO-St nanocomposite to epoxy, it can be inferred that the network becomes tougher in the elastic region and then becomes softer passing this region. Mechanistic sketches of epoxy network formation in the presence of bare and surface-treated nanoparticles are discussed.

Cytowania

  • 4 1

    CrossRef

  • 0

    Web of Science

  • 4 3

    Scopus

Autorzy (7)

  • Zdjęcie użytkownika  Morteza Ganjaee

    Morteza Ganjaee

    • Institute for Color Science and Technology Department of Nanomaterials and Nanocoatings
  • Zdjęcie użytkownika  Henri Vahabi

    Henri Vahabi

    • Université de Lorraine, Laboratoire MOPS
  • Zdjęcie użytkownika  Xavier Gabrion

    Xavier Gabrion

    • FEMTO-ST Institute, Department of Applied Mechanics, UMR 6176, University Bourgogne-Franche-Comté, CNRS/ENSMM/UFC/UTBM
  • Zdjęcie użytkownika  Pascal Laheurte

    Pascal Laheurte

    • Universite de Lorraine, Laboratoire LEM3
  • Zdjęcie użytkownika  Payam Zarrintaj

    Payam Zarrintaj

    • University of Tehran College of Engineering, School of Chemical Engineering
  • Zdjęcie użytkownika  Mohammad Saeb

    Mohammad Saeb

    • Institute for Color Science and Technology Department of Resin and Additives

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuł w czasopiśmie wyróżnionym w JCR
Opublikowano w:
PROGRESS IN ORGANIC COATINGS nr 119, strony 171 - 182,
ISSN: 0300-9440
Język:
angielski
Rok wydania:
2018
Opis bibliograficzny:
Ganjaee M., Vahabi H., Gabrion X., Laheurte P., Zarrintaj P., Formela K., Saeb M.: An attempt to mechanistically explain the viscoelastic behavior of transparent epoxy/starch-modified ZnO nanocomposite coatings// PROGRESS IN ORGANIC COATINGS. -Vol. 119, (2018), s.171-182
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.porgcoat.2018.02.016
Weryfikacja:
Politechnika Gdańska

wyświetlono 140 razy

Publikacje, które mogą cię zainteresować

Meta Tagi