Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
Abstrakt
The paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed monitoring of the natural corrosion process without external current (IDC = 0A) nor potential perturbation of the system. The results proved the usefulness of measurements of actual electrochemical systems at zero external current conditions. It was found that a transition to an active state occurred for relatively high strain rates, while the passive layer cracking process did not depend on the strain rate.
Cytowania
-
0
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (7)
-
Maciej Kalinowski
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
ELECTROCHIMICA ACTA
nr 469,
ISSN: 0013-4686 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Orlikowski J., Jurak K., Darowicki K., Szociński M., Karólkowska A., Wysmułek S., Kalinowski M.: Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain// ELECTROCHIMICA ACTA -Vol. 469, (2023), s.143252-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.electacta.2023.143252
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 90 razy