This study presents results of experimental tests on quality of dissimilar welded joints between 316L austenitic and 2304 lean duplex stainless steels, welded without ceramic backing. Fiber laser welded butt joints at a thickness of 8 mm were subjected to non‐destructive testing (visual and penetrant), destructive testing (static tensile test, bending test, and microhardness measurements) and structure observations (macro‐ and microscopic examinations, SEM, element distribution characteristics, and ferrite content measurements). Non‐destructive tests and metallographic examinations showed that the welded joints meet the acceptance criteria for B level in accordance with EN ISO 13919–1 standard. Also the results of the destructive tests confirmed the high quality of the joints: specimens were fractured in base material with lower strength—316L austenitic stainless steel and a 180° bending angle was obtained confirming the high plasticity of the joints. Microscopic examination, SEM and EDS analysis showed the distribution of alloying elements in joints. The microhardness of the autogenous weld metal was higher by about 20 HV0.2 than that of the lean duplex steel. Ferrite content in the root was about 37% higher than in the face of the weld. The Schaeffler phase diagram was used to predict the phase composition of the welded joints and sufficient compliance with the magnetic method was found. The presented procedure can be used for welding of 316L–2304 stainless steels dissimilar welded joints of 8 mm thickness without ceramic backing.
Cytowania
-
7 3
CrossRef
-
0
Web of Science
-
7 5
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma13132930
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 13,
strony 1 - 16,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2020
- Opis bibliograficzny:
- Landowski M., Świerczyńska A., Rogalski G., Fydrych D.: Autogenous Fiber Laser Welding of 316L Austenitic and 2304 Lean Duplex Stainless Steels// Materials -Vol. 13,iss. 13 (2020), s.1-16
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma13132930
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 206 razy
Publikacje, które mogą cię zainteresować
Laser Dissimilar Welding of AISI 430F and AISI 304 Stainless Steels
- K. Pańcikiewicz,
- A. Świerczyńska,
- P. Hućko
- + 1 autorów
Effects of preheating on laser beam–welded NSSC 2120 lean duplex steel
- M. Landowski,
- S. C. Simon,
- C. Breznay
- + 2 autorów