CGO as a barrier layer between LSCF electrodes and YSZ electrolyte fabricated by spray pyrolysis for solid oxide fuel cells
Abstrakt
Perovskite La0.6Sr0.4Co0.2Fe0.8O3 − δ (LSCF) is often used as a cathode material for solid oxide fuel cells (SOFC) due to high mixed ionic and electronic conductivity and good catalytic activity. Unfortunately, sintering of the LSCF cathode together with the yttria stabilized zirconia (YSZ) electrolyte, leads to formation of the La2Zr2O7 and SrZrO3 phases in the interface. These phases increase the resistance of the cell. To avoid creation of the undesirable phases, diffusion barrier layers are often used. In this work 200 nm thick cerium-gadolinium oxide (CGO) layer deposited by spray pyrolysis is used as a diffusion barrier. The impact of sintering temperature on the effectiveness of diffusion barrier was examined. For optimized sintering temperature of 900 °C, the CGO barrier layer leads to lowering polarization loses of almost two orders of magnitude from 477 mΩ cm2 (when CGO is not used) to 7 mΩ cm2.
Cytowania
-
2 3
CrossRef
-
0
Web of Science
-
2 5
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
SOLID STATE IONICS
nr 302,
strony 113 - 117,
ISSN: 0167-2738 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Szymczewska D., Karczewski J., Chrzan A., Jasiński P.: CGO as a barrier layer between LSCF electrodes and YSZ electrolyte fabricated by spray pyrolysis for solid oxide fuel cells// SOLID STATE IONICS. -Vol. 302, (2016), s.113-117
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.ssi.2016.11.008
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 174 razy