Comparative Study of the Reinforcement Type Effect on the Thermomechanical Properties and Burning of Epoxy-Based Composites
Abstrakt
Aramid (AF), glass (GF), carbon (CF), basalt (BF), and flax (FF) fibers in the form of fabrics were used to produce the composites by hand-lay up method. The use of fabrics of similar grammage for composites’ manufacturing allowed for a comprehensive comparison of the properties of the final products. The most important task was to prepare a complex setup of mechanical and thermomechanical properties, supplemented by fire behavior analysis, and discuss both characteristics in their application range. The mechanical properties were investigated using tensile and flexural tests, as well as impact strength measurement. The investigation was improved by assessing thermomechanical properties under dynamic deformation conditions (dynamic mechanical–thermal analysis (DMTA)). All products were subjected to a fire test carried out using a cone calorimeter (CC).
Cytowania
-
9
CrossRef
-
0
Web of Science
-
1 1
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Journal of Composites Science
nr 5,
ISSN: - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Salasinska K., Barczewski M., Aniśko J., Hejna A., Celiński M.: Comparative Study of the Reinforcement Type Effect on the Thermomechanical Properties and Burning of Epoxy-Based Composites// Journal of Composites Science -Vol. 5,iss. 3 (2021), s.89-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/jcs5030089
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 119 razy
Publikacje, które mogą cię zainteresować
Mechanical Properties of Bio-Composites Based on Epoxy Resin and Nanocellulose Fibres
- M. Roszowska-Jarosz,
- J. Masiewicz,
- M. Kostrzewa
- + 4 autorów
Thermomechanical and Fire Properties of Polyethylene-Composite-Filled Ammonium Polyphosphate and Inorganic Fillers: An Evaluation of Their Modification Efficiency
- M. Barczewski,
- A. Hejna,
- K. Sałasińska
- + 4 autorów