Abstrakt
Carbon nanostructured films were synthesized by chemical vapor deposition (CVD) on H18 stainless steel (AISI 440C) sheets with an H2/CH4/N2 gas mixture at various substrate temperatures. During the synthesis, the iron and chromium oxide layer was formed between the steel and carbonaceous layer. The carbon films exhibited wall-like and spherical morphologies and structures, as characterized by scanning electron microscopy and Raman spectroscopy. It was found that the synthesis temperature affects the microsphere density and, therefore, also in the electrochemical behavior. The electrochemical behavior of nanostructured carbon coatings strongly depends on the CVD deposition conditions. The best corrosion resistance (Rp = 11.8 MΩ·cm2, Icorr = 4.4 nA·cm−2) exhibits a nanostructured carbon sample with a moderate amount of sp2-C-rich carbon microspheres CμSs synthesized at 700 °C. The corrosion resistance of the nanostructured carbon coating is better than raw stainless steel.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
1
Scopus
Autorzy (3)
-
Mirosław Sawczak dr hab. inż.
- Insytut Maszyn Przepływowych
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/coatings11111403
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Coatings
nr 11,
ISSN: 2079-6412 - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Pierpaoli M., Sawczak M., Dettlaff A.: Development of Microstructured Carbon Coatings by Substrate-Catalytic CVD// Coatings -Vol. 11,iss. 11 (2021), s.1403-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/coatings11111403
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 131 razy