Abstrakt
The effect of a natural filler (diatomaceous earth [DE], a promising drug-delivery agent) and its content was investigated on the performance of a model glass-ionomer cement (GIC). Three sample series, differing in DE content (0, 2.5 and 5 wt%), were prepared using a commercial GIC as a matrix (3M Ketac Molar Easymix). The resultant surface microhardness and roughness, wear performance, and compressive strength of the samples were measured after the samples had been stored in deionized water at 37°C for a fixed time. Moreover, the film thickness was tested for the freshly mixed samples. The numerical data was subjected to statistical analysis, in order to test the null hypotheses of the equality of the measured properties between the reference and the DE-modified samples. According to the results, diatomaceous earth particles are uniformly distributed in the GIC matrix, and the cavities of frustules tend to be filled with the GIC. This translates into the observed performance of the DE-loaded GIC. Compared with the reference material (0 wt% DE), the surface microhardness (2.5 wt% DE, p = 0.014; 5 wt% DE, p = 0.005) and roughness (e.g. Ra; 2.5 wt% DE, p = 0.003; 5 wt% DE, p < 0.001) are increased. No effect on the wear performance (p = 0.530 and 0.256, respectively) or compressive strength (p = 0.514) was noticed in the case of DE partially substituting the glass phase. Based on the study results, it is evidenced that diatom frustules are a suitable filler for application in conventional glass-ionomer cements as the glass-substituting drug-loaded carrier. Notably, however, the surface finish method of the DE-filled materials needs development.
Cytowania
-
7
CrossRef
-
0
Web of Science
-
6
Scopus
Autorzy (6)
-
Magdalena Łępicka dr inż
- Institute of Mechanical Engineering, Faculty of Mechanical Engineering, Bialystok University of Technolog
-
Magdalena Rodziewicz
- Bialystok University of Technology
-
Michał Kawalec dr inż.
- Institute of Mechanical Engineering, Faculty of Mechanical Engineering, Bialystok University of Technolog
-
Klaudia Nowicka
- Institute of Mechanical Engineering, Faculty of Mechanical Engineering, Bialystok University of Technolog
-
Jan Krzysztof Kurzydłowski
- Institute of Mechanical Engineering, Faculty of Mechanical Engineering, Bialystok University of Technolog
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jmbbm.2022.105324
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Journal of the Mechanical Behavior of Biomedical Materials
nr 133,
ISSN: 1751-6161 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Łępicka M., Rodziewicz M., Kawalec M., Nowicka K., Tsybrii Y., Kurzydłowski J. K.: Diatomaceous earth as a drug-loaded carrier in a glass-ionomer cement// Journal of the Mechanical Behavior of Biomedical Materials -Vol. 133, (2022), s.105324-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jmbbm.2022.105324
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 131 razy
Publikacje, które mogą cię zainteresować
Study on Dry Sliding Wear and Friction Behaviour of Al7068/Si3N4/BN Hybrid Composites
- K. Subramanian,
- S. Murugesan,
- D. G. Mohan
- + 1 autorów
Rotational Molding of Linear Low-Density Polyethylene Composites Filled with Wheat Bran
- A. Hejna,
- M. Barczewski,
- J. Andrzejewski
- + 4 autorów
Rotational molding of polylactide (PLA) composites filled with copper slag as a waste filler from metallurgical industry
- M. Barczewski,
- A. Hejna,
- J. Aniśko
- + 6 autorów