Abstrakt
Laser surface treatment conducted at different power levels is an option to modify titanium bone implants to produce nano- and microtopography. However, such processing can lead to excess mechanical stress within the surface layer. This research aims to calculate the level of such residual stresses after the surface processing of Ti grade IV, Ti15Mo, and Ti6Al7Nb alloys with an Nd:YAG laser. Light and scanning electron microscopies (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffractometry (XRD), optical profilography, and nano-indentation tests were applied to characterize the surface zone. The laser processing resulted in a distinct surface pattern and the formation of remelted zones 66–126 μm thick, with roughness values ranging between 0.22 and 1.68 μm. The mechanical properties were weakly dependent on the material composition. The residual stresses caused by the laser treatment were moderate, always tensile, increasing with loading, and was the highest for the Ti15Mo alloy.
Cytowania
-
4
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/app13106276
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Applied Sciences-Basel
nr 13,
ISSN: 2076-3417 - Język:
- angielski
- Rok wydania:
- 2023
- Opis bibliograficzny:
- Jażdżewska M., Bartmański M., Zieliński A., Kwidzińska D.: Effect of Laser Treatment on Intrinsic Mechanical Stresses in Titanium and Some of Its Alloys// Applied Sciences-Basel -Vol. 13,iss. 10 (2023), s.6276-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/app13106276
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 99 razy