Effect of the Post-Weld Surface Condition on the Corrosion Resistance of Austenitic Stainless Steel AISI 304
Abstrakt
Surfaces of welded elements made of corrosion-resistant (stainless) steels develop temper colours. The removal of thickened oxide layers off steels exposed to temperatures below 300°C is necessary and entails the restoring of high corrosion resistance of the stainless steel. The article presents tests concerned with the effect of a method applied to remove post-weld temper on the corrosion resistance of austenitic stainless steel AISI 304. It was ascertained that the most favourable method enabling the obtainment of high corrosion resistance involved the use of an appropriate passivation process.
Cytowania
-
1
CrossRef
-
0
Web of Science
-
0
Scopus
Autorzy (4)
Cytuj jako
Pełna treść
pobierz publikację
pobrano 31 razy
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.17729/ebis.2018.1/2
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach recenzowanych i innych wydawnictwach ciągłych
- Opublikowano w:
-
Biuletyn Instytutu Spawalnictwa w Gliwicach
wydanie 1,
strony 17 - 23,
ISSN: 0867-583X - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Rogalski G., Jurkowski M., Łabanowski J., Fydrych D.: Effect of the Post-Weld Surface Condition on the Corrosion Resistance of Austenitic Stainless Steel AISI 304// Biuletyn Instytutu Spawalnictwa w Gliwicach. -., iss. 1 (2018), s.17-23
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.17729/ebis.2018.1/2
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 162 razy
Publikacje, które mogą cię zainteresować
Hydrogen Damage in Superaustenitic 904L Stainless Steels
- J. Michalska,
- B. Chmiela,
- J. Łabanowski
- + 1 autorów
2014