Abstrakt
High-temperature oxide melt solution calorimetry was used to investigate energetics of a series of rare earth niobates RE3NbO7. All of investigated compounds were found to be stable in enthalpy in respect to their oxides. The enthalpy of formation from oxides becomes more exothermic as the size of the RE cation increases, a trend seen previously in other RE compounds including pyrochlores, perovskites, and phosphates. For smaller RE cations the enthalpy of exchange of RE between niobates and titanates is close to zero, whereas larger RE are energetically favored in the titanate pyrochlores. Implications of the results from the geochemical and material engineering points of view are discussed.
Cytowania
-
2 0
CrossRef
-
0
Web of Science
-
2 1
Scopus
Autorzy (2)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
AMERICAN MINERALOGIST
nr 100,
strony 1578 - 1583,
ISSN: 0003-004X - Język:
- angielski
- Rok wydania:
- 2015
- Opis bibliograficzny:
- Mielewczyk-Gryń A. D., Navrotsky A.: Enthalpies of formation of rare earth niobates, RE3NbO7// AMERICAN MINERALOGIST. -Vol. 100, iss. 7 (2015), s.1578-1583
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.2138/am-2015-5210
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 114 razy
Publikacje, które mogą cię zainteresować
Formation enthalpies of LaLn׳O3 (Ln׳=Ho, Er, Tm and Yb) interlanthanide perovskites
- J. Qi,
- X. Guo,
- A. D. Mielewczyk-Gryń
- + 1 autorów
Conductivity, structure, and thermodynamics of Y2Ti2O7–Y3NbO7 solid solutions
- P. Winiarz,
- A. Mielewczyk-Gryń,
- K. Lilova
- + 6 autorów