Eu3+ doped tellurite glass ceramics containing SrF2 nanocrystals: Preparation, structure and luminescence properties
Abstrakt
Eu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after annealing at 370 °C. FTIR studies revealed absorption bands in the range of 500–850 cm−1 characteristic to TeO2 glasses. Obtained materials exhibited emission originated from the 5DJ (J = 0–2) to the 7FJ (J = 0–4) transitions of Eu3+ ions under 395 and 465 nm excitations. TRES measurements indicated presence of two different surroundings of the Eu3+ ions. In glass ceramics samples longer lifetimes of 615 nm emission of Eu3+ were achieved in comparison to the precursor glass.
Cytowania
-
3 7
CrossRef
-
0
Web of Science
-
3 8
Scopus
Autorzy (6)
-
Anna Synak
- Uniwersytet Gdański/ Wydział Matematyki, Fizyki i Informatyki Instytut Fizyki Doświadczalnej
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
JOURNAL OF ALLOYS AND COMPOUNDS
nr 696,
strony 619 - 626,
ISSN: 0925-8388 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Walas M., Lewandowski T., Synak A., Łapiński M., Sadowski W., Kościelska B.: Eu3+ doped tellurite glass ceramics containing SrF2 nanocrystals: Preparation, structure and luminescence properties// JOURNAL OF ALLOYS AND COMPOUNDS. -Vol. 696, (2016), s.619-626
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.jallcom.2016.11.301
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 310 razy