Fabrication of anti-corrosion nitrogen doped graphene oxide coatings by electrophoretic deposition

Abstrakt

This work assesses anti-corrosion properties of graphene and N-doped graphene coatings deposited on copper by an electrophoretic method. Graphene oxide (GO) precursor was synthesized by an improved Hummers' method, whereas N-doping was performed hydrothermally in the presence of ammonia. After nitrogenation, doped graphene oxide samples (NGO) contained a reduced amount of oxygen and about 9% w/w nitrogen as pyridinic, pyrrole, and graphitic groups. Nevertheless, it was possible to obtain a stable aqueous dispersion of NGOs, a prerequisite for the EPD process. According to SEM images, the EPD coatings were compact with minor defects. On the contrary, GO coating possessed cracks and large pores that resulted from gas evolution during electrolysis. Electrochemical studies showed that all coatings prevented copper from corrosion in saline solution, however, the nitrogenated coatings did not exhibit better anti-corrosion properties than reduced graphene oxide coating. A reasonable explanation of this finding is that some positive properties of the nitrogenated coatings, in terms of anti-corrosion action, like low hydrophilicity and good adhesion, were counteracted by their catalytic activity towards oxygen reduction reaction.

Cytowania

  • 3 0

    CrossRef

  • 0

    Web of Science

  • 3 3

    Scopus

Autorzy (4)

Cytuj jako

Pełna treść

pełna treść publikacji nie jest dostępna w portalu

Słowa kluczowe

Informacje szczegółowe

Kategoria:
Publikacja w czasopiśmie
Typ:
artykuły w czasopismach
Opublikowano w:
APPLIED SURFACE SCIENCE nr 499, strony 1 - 7,
ISSN: 0169-4332
Język:
angielski
Rok wydania:
2020
Opis bibliograficzny:
Ollik K., Rybarczyk M., Karczewski J., Lieder M.: Fabrication of anti-corrosion nitrogen doped graphene oxide coatings by electrophoretic deposition// APPLIED SURFACE SCIENCE -Vol. 499, (2020), s.1-7
DOI:
Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.apsusc.2019.143914
Weryfikacja:
Politechnika Gdańska

wyświetlono 252 razy

Publikacje, które mogą cię zainteresować

Applying of Doped Graphene Oxide Coatings for Corrosion Prevention

2019

The protective properties of graphene oxide coatings functionalized with phosphorus atoms.

2021

Functionalization of graphene oxide coatings with phosphorus atoms and their corrosion resistance in sodium chloride environment

2021

Effect of Functionalization of Reduced Graphene Oxide Coatings with Nitrogen and Sulfur Groups on Their Anti-Corrosion Properties

2021
Meta Tagi