Highly sensitive large strain cellulose/multiwalled carbon nanotubes (MWCNTs)/thermoplastic polyurethane (TPU) nanocomposite foams: From design to performance evaluation
Abstrakt
Aerogel-based polymer composite foams are promising for large strain piezoresistive sensors, but their aerogel skeleton is partially destroyed during the foaming process, limiting their sensitivity. Herein, the thermoplastic polyurethane was synthesized on the aerogel skeleton to obtain cellulose/multiwalled carbon nanotubes (MWCNTs)/thermoplastic polyurethane (TPU) nanocomposite materials foamed with the aid of supercritical carbon dioxide (ScCO2). A series of lightweight, high strength, and high sensitivity nanocomposite foams were developed, possessing an average diameter of ~9.11 μm and a cell density of 6.84×108 cells/cm3. The mechanical properties, including compressive strength and compressive modulus, were promisingly 5.56 and 28.90 MPa, respectively. Under 50% strain, apparent high repeatability of force-to-electricity conversion behavior was detected in 100 compression cycles.
Cytowania
-
1 8
CrossRef
-
0
Web of Science
-
1 8
Scopus
Autorzy (11)
-
Yanpei Fei
- Zhejiang University of Technology
-
Ruitao Jiang
- Zhejiang University of Technology
-
Wei Fang
- Zhejiang University of Technology
-
Tong Liu
- Zhejiang University of Technology
-
Morteza Ehsani
- Iran Polymer and Petrochemical Institute
-
Mateusz Barczewski
- Politechnika Poznańska
-
S. Mohammad Sajadi
- Cihan University-Erbil
-
Feng Chen
- Zhejiang University of Technology
-
Tairong Kuang
- Zhejiang University of Technology
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
JOURNAL OF SUPERCRITICAL FLUIDS
nr 188,
ISSN: 0896-8446 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Fei Y., Jiang R., Fang W., Liu T., Saeb M., Hejna A., Ehsani M., Barczewski M., Sajadi S. M., Chen F., Kuang T.: Highly sensitive large strain cellulose/multiwalled carbon nanotubes (MWCNTs)/thermoplastic polyurethane (TPU) nanocomposite foams: From design to performance evaluation// JOURNAL OF SUPERCRITICAL FLUIDS -Vol. 188, (2022), s.105653-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.supflu.2022.105653
- Źródła finansowania:
-
- Publikacja bezkosztowa
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 86 razy
Publikacje, które mogą cię zainteresować
Ultrafast high-temperature sintering (UHS) of cerium oxide-based compound
- A. Kabir,
- B. Lemieszek,
- J. Karczewski
- + 4 autorów