: Sodium-calcium-phosphate based oxynitride glasses and glass-ceramics doped with Mg, Si, and Nb were studied in vitro in simulated body fluid (SBF) under static conditions. The release of ions and pH changes up to 7 days of immersion were investigated. The nitrogen incorporation into phosphate glass matrix was found to notably influence in vitro dissolution only of homogenous glasses. Increasing the nitrogen content in the samples decreased the mean mass loss, while the niobate incorporation increased it. The correlation between the nitrogen content and increase in pH of SBF was also observed. The presence of phosphates crystallites was found to support the dissolution process at the beginning step (up to 3 days).
Cytowania
-
3
CrossRef
-
0
Web of Science
-
3
Scopus
Autorzy (5)
-
Polina Sinitsyna
-
Sharafat Ali profesor
-
Leena Hupa profesor
-
Bo Jonson profesor
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma14237425
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 14,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2021
- Opis bibliograficzny:
- Wójcik N., Sinitsyna P., Ali S., Hupa L., Jonson B.: In Vitro Dissolution of Na-Ca-P-Oxynitrides// Materials -,iss. 14 (2021), s.7425-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma14237425
- Źródła finansowania:
-
- IDUB
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 107 razy