Influence of laser processing of the low alloy medium carbon structural steel on the development of the fatigue crack
Abstrakt
The paper contains the results of the structural analysis, hardness tests and fatigue tests conducted for the medium carbon structural steel with low content of Cr and Ni after its processing with CO2 laser beam. Pre-cracks were made in the round compact tension (RCT) specimen used for fatigue test. Next, four paths, parallel to each other, were melted on both sides of the samples using a laser beam. The paths were perpendicular to the direction of the axis of the cut notch. The first melted path ran at a distance of about 2.5 mm from the pre crack tip. Fatigue test results were compared with the sample which was not subjected to laser treatment. The fatigue tests showed that the sample with no laser treatment fractured after 270,000 cycles and the laser treated sample was able to withstand 7.2 million cycles for the same load and during this time the crack length increased only 0.4 mm. Hardness tests to estimate the residual internal stresses in the melted zone, in the heat affected zone (HAZ) and in the native material were carried out using nanoindenter. It was shown that compressive residual stress, in native material, close to HAZ in half-length of the melted path, just before the front of the crack, was 1165 MPa. These residual stresses contribute to the stopping of the development of the fatigue crack. It was also shown that the longitudinal manganese sulfide inclusions reduce crack development rate probably by blunting the crack blade.
Cytowania
-
9
CrossRef
-
0
Web of Science
-
1 1
Scopus
Autorzy (2)
-
Anna Bień Dr Inż.
- . .
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.surfcoat.2016.04.032
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
SURFACE & COATINGS TECHNOLOGY
nr 296,
strony 117 - 123,
ISSN: 0257-8972 - Język:
- angielski
- Rok wydania:
- 2016
- Opis bibliograficzny:
- Szkodo M., Bień A.: Influence of laser processing of the low alloy medium carbon structural steel on the development of the fatigue crack// SURFACE & COATINGS TECHNOLOGY. -Vol. 296, (2016), s.117-123
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.surfcoat.2016.04.032
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 141 razy
Publikacje, które mogą cię zainteresować
Effect of selective laser treatment on initiation of fatigue crack in the main part of an undercarriage drag strut
- A. Bień,
- M. Szkodo,
- J. Doberski
- + 1 autorów