Wyszukiwarka
Abstrakt
The Ti13Zr13Nb alloy in solid and porous form was oxidised. The constant voltage 20 V, oxidation time 0.5 and 1 h, and 1 M H3PO4 (orthophosphoric acid) with addition of HF (hydrofluoric acid) as a test solution were applied. SEM (Scanning Electron Microscope) examinations of surface, EDS (Energy Dispersive X-ray Spectroscopy) chemical analysis, nanohardness and nano-scratch tests, and corrosion potentiokinetic tests at various pH were performed. The results show that oxidation of this ternary alloy in acidic solution in presence of fluoride ions results in an appearance of nanotubular oxide layer of high nanohardness, well adjacent to the base but relatively easily damaged in scratch test. Different colonies of nanotubes are observed, related to different phases of the alloy.
Autorzy (4)
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
SURFACE & COATINGS TECHNOLOGY
nr 258,
strony 1239 - 1248,
ISSN: 0257-8972 - Język:
- angielski
- Rok wydania:
- 2014
- Opis bibliograficzny:
- Ossowska A., Sobieszczyk S., Supernak-Marczewska M., Zieliński A.: Morphology and properties of nanotubular oxide layer on the Ti13Zr13Nb alloy// SURFACE & COATINGS TECHNOLOGY. -Vol. 258, (2014), s.1239-1248
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 125 razy
Publikacje, które mogą cię zainteresować
Influence of Two-Stage Anodization on Properties of the Oxide Coatings on the Ti–13Nb–13Zr Alloy
- A. Ossowska,
- A. Zieliński,
- J. Olive
- + 2 autorów