Previously unreported σ-phases in the ternary niobium-based systems Nb–X–Ga for X = Ru, Rh, Pd, Ir, Pt, Au, and Nb–X–Al for X = Ir, and Pt are presented, prepared by arc-melting followed by annealing at 1000 °C for 1 week. The phases are primitive tetragonal (P42/mnm, no. 136) with lattice parameters of a = 9.8336(2)–9.9432(1) Å and c = 5.1098(1)–5.1718(1) Å. Refinements of the single crystal X-ray diffraction data for the Ru and Ir containing materials gave the formulas Nb20Ru5Ga5 and Nb20Ir4Ga6, showing mixing of X/Ga on the crystallographic 8i2 and 2a sites of the structure, a type of disorder frequently found in σ-phases. We present a graphical classification for ternary σ-phases that places our materials in context with previous materials. The materials do not show evidence of bulk superconductivity above 2 K. Synthesis of equivalent Ta-based σ-phases was attempted but they were not found.
Cytowania
-
2
CrossRef
-
0
Web of Science
-
2
Scopus
Autorzy (4)
-
Elizabeth M. Carnicom
-
Weiwei Xie
-
Robert J. Cava
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
DALTON TRANSACTIONS
nr 46,
wydanie 41,
strony 14158 - 14163,
ISSN: 1477-9226 - Język:
- angielski
- Rok wydania:
- 2017
- Opis bibliograficzny:
- Carnicom E., Xie W., Klimczuk T., Cava R.: New σ-phases in the Nb–X–Ga and Nb–X–Al systems (X = Ru, Rh, Pd, Ir, Pt, and Au)// DALTON TRANSACTIONS. -Vol. 46, iss. 41 (2017), s.14158-14163
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1039/c7dt02955a
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 101 razy