Niobate in silicate and phosphate glasses: Effect of glass basicity on crucible dissolution

Natalia Anna Wójcik; Sharafat Ali; Efstratios Kamitsos; Doris Möncke

doi:10.1111/ijag.16505

Niobate in silicate and phosphate glasses: Effect of glass basicity on crucible dissolution

Abstrakt

Using niobium crucibles for melting phosphate and silicate glasses of various modifier oxide contents, and therefore varying optical basicity (Λ), was found to result in varying dissolution rates of niobate during melting. Because of their high electronic polarizability, even small concentrations of niobates are detectable in the Raman spectra of glasses. Even less than 1 mol% Nb2O5 can be identified, as independently confirmed by SEM‐EDX analysis. Silica‐rich glasses (~60 % SiO2, Λ~0.6) did not show significant Nb dissolution from the crucible, while higher basicity metasilicate glasses (~ 50% SiO2, Λ~0.65) and pyrophosphate glasses (~30% P2O5, Λ~0.7) did show the typical niobate signature in the Raman spectra at 810‐840 cm‐1, depending on composition. While niobium is well dissolved throughout the pyrophosphate glass, metasilicate glasses showed a much more intense Raman signature of niobate units near the outer surface of the glass. Measurements along the cross section of a fractured metasilicate glass showed a steady decrease of the strength of the niobate signature from the surface toward the bulk of the material. Besides correlation with optical basicity, the tendency of melts to dissolve Nb crucible was discussed in terms of the connectivity or polymerization of the network and the corresponding melt viscosity.

Cytowania

1 3

CrossRef
0

Web of Science
1 4

Scopus

Autorzy (4)

Natalia Anna Wójcik (dawniej: Natalia Wójcik) dr hab. inż.
Sharafat Ali profesor
Efstratios Kamitsos profesor
Doris Möncke profesor

Cytuj jako

Pełna treść

pobierz publikację

pobrano 64 razy

Wersja publikacji: Accepted albo Published Version
DOI:: Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1111/ijag.16505
Licencja: otwiera się w nowej karcie

Słowa kluczowe

Informacje szczegółowe

Kategoria:

Publikacja w czasopiśmie

Typ:

artykuły w czasopismach

Opublikowano w:

International Journal of Applied Glass Science nr 13, strony 121 - 134,
ISSN: 2041-1286

Język:

angielski

Rok wydania:

2022

Opis bibliograficzny:

Wójcik N., Ali S., Kamitsos E., Möncke D.: Niobate in silicate and phosphate glasses: Effect of glass basicity on crucible dissolution// International Journal of Applied Glass Science -Vol. 13,iss. 1 (2022), s.121-134

DOI: