The Pr-TiO2 nanoparticles were prepared by using the sol-gel method. As-prepared samples were characterized by BET measurements, X-ray powder diffraction analysis (XRD) and UV-Vis spectra. Visible and ultraviolet light photocatalytic activity of the sample was studied by photodegradation of phenol while considering the influence of the dopant concentration. TiO2 doped with 0.25 mol% of praseodymium showed the highest photocatalytic activity under visible light irradiation. Pr-TiO2 had anatase structure. The surface area was higher for powders with higher content of rare earth metal ion, and ranged from 121 to 150 m2/g. Red shifts of the absorption edge toward the visible region were observed for the doped samples compared to pure TiO2.
Autorzy (4)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
Physicochemical Problems of Mineral Processing
nr 50,
wydanie 2,
strony 515 - 525,
ISSN: 1643-1049 - Język:
- angielski
- Rok wydania:
- 2013
- Opis bibliograficzny:
- Reszczyńska J., Arenas Esteban D., Gazda M., Zaleska-Medynska A.: Pr-doped TiO2: The effect of metal content on photocatalytic activity// Physicochemical Problems of Mineral Processing. -Vol. 50, iss. 2 (2013), s.515-525
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 134 razy
Publikacje, które mogą cię zainteresować
Lanthanide co-doped TiO2: the effect of metal type and amount on surface properties and photocatalytic activity
- J. Reszczyńska,
- T. Grzyb,
- J. W. Sobczak
- + 4 autorów
Fotokatalityczne uzdatnianie wody basenowej = Photocatalytic treatment of swimming pool water
- J. Hupka,
- M. Janczarek,
- A. Hänel
- + 3 autorów