Praseodymium Orthoniobate and Praseodymium Substituted Lanthanum Orthoniobate: Electrical and Structural Properties
Abstrakt
In this paper, the structural properties and the electrical conductivity of La1−xPrxNbO4+δ (x = 0.00, 0.05, 0.1, 0.15, 0.2, 0.3) and PrNbO4+δ are presented and discussed. All synthesized samples crystallized in a monoclinic structure with similar thermal expansion coefficients. The phase transition temperature between the monoclinic and tetragonal structure increases with increasing praseodymium content from 500 ◦C for undoped LaNbO4+δ to 700 ◦C for PrNbO4+δ. Thermogravimetry, along with X-ray photoelectron spectroscopy, confirmed a mixed 3+/4+ oxidation state of praseodymium. All studied materials, in humid air, exhibited mixed protonic, oxygen ionic and hole conductivity. The highest total conductivity was measured in dry air at 700 ◦C for PrNbO4+δ, and its value was 1.4 · 10−3 S/cm.
Cytowania
-
5
CrossRef
-
0
Web of Science
-
5
Scopus
Autorzy (5)
Cytuj jako
Pełna treść
- Wersja publikacji
- Accepted albo Published Version
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma15062267
- Licencja
-
otwiera się w nowej karcie
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuły w czasopismach
- Opublikowano w:
-
Materials
nr 15,
ISSN: 1996-1944 - Język:
- angielski
- Rok wydania:
- 2022
- Opis bibliograficzny:
- Dzierzgowski K., Wachowski S., Łapiński M., Mielewczyk-Gryń A., Gazda M.: Praseodymium Orthoniobate and Praseodymium Substituted Lanthanum Orthoniobate: Electrical and Structural Properties// Materials -Vol. 15,iss. 6 (2022), s.2267-
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.3390/ma15062267
- Źródła finansowania:
-
- OPUS 2016/23/B/ST5/02137
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 133 razy