New rare earth-doped K2Ta2O6 photocatalysts were successfully synthesized by hydrothermal method. The effect of dopant type (Y,Yb,Ho,Pr,Er) and amount of rare earth precursor (2,4,8 and 10 mol%) on the physicochemical and photocatalytic properties of RE-K2Ta2O6 have been investigated. All as-prepared materials were characterized by UV–vis diffuse reflectance spectroscopy, Brunauer-Emmett-Teller specific surface area measurement, scanning electron microscopy with energy dispersive X-ray spectroscopy, powder X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, magnetic susceptometry and photoluminescence emission spectroscopy. The photocatalytic activity under UV–vis light irradiation was estimated in phenol degradation in aqueous phase, toluene removal in gas phase and H2 generation from formic acid solution. The experimental results show that, novel RE-K2Ta2O6 exhibits greatly improved degradation efficiency under UV–vis light irradiation compared with pristine K2Ta2O6. The Er-K2Ta2O6 and Pr-K2Ta2O6, obtained by introducing of 2 mol% of RE ions during synthesis, reveal the highest photocatalytic activity among prepared samples in aqueous phase (33% of PhOH decomposition after 90 min of irradiation) and gas phase (45% of toluene removal after 60 min), respectively. Moreover, both photocatalysts present good stability after subsequent three cycles. The active species trapping test shows that OH and O2− radicals are significantly involved in phenol oxidation under UV–vis light. The amount of H2 evolution increases with addition of Er dopant. The highest H2 production is obtained for 10 mol% Er-K2Ta2O6 after 240 min of UV–vis light irradiation (15.4 μmol/min). Enhanced photoactivity performance can be attributed to incorporation of RE ions at K+ lattice site in RE-K2Ta2O6, probably leading to formation of new RE 4f states below the conduction band of K2Ta2O6 structure. To investigate the localization of RE ions in K2Ta2O6 structure, the band structure and partial density of the states have been investigated. Computer simulations were performed using plane-wave based Vienna ab-initio simulation package with the generalized gradient approximation by Perdew-Burke-Ernzerho. Moreover, inclusion of RE ions in K2Ta2O6 causes predominance of pyrochlore phase formation over perovskite.
Cytowania
-
4 9
CrossRef
-
0
Web of Science
-
4 4
Scopus
Autorzy (10)
-
Anna Krukowska mgr inż.
- Faculty of Chemistry, University of Gdansk Department of Environmental Technology
-
Wojciech Lisowski
- Institute of Physical Chemistry, Polish Academy of Sciences -
-
Alicja Mikolajczyk
- Faculty of Chemistry, University of Gdansk Laboratory of Environmental Chemometrics
-
Henry P. Pinto
- chool of Physical Sciences and Nanotechnology, Yachay Tech University -
-
Tomasz Puzyn
- Faculty of Chemistry, University of Gdansk Laboratory of Environmental Chemometrics
-
Tomasz Grzyb
- Faculty of Chemistry, Adam Mickiewicz University Department of Rare Earths
-
Adriana Zaleska-Medynska
- Faculty of Chemistry, University of Gdansk Department of Environmental Technology
Cytuj jako
Pełna treść
pełna treść publikacji nie jest dostępna w portalu
Słowa kluczowe
Informacje szczegółowe
- Kategoria:
- Publikacja w czasopiśmie
- Typ:
- artykuł w czasopiśmie wyróżnionym w JCR
- Opublikowano w:
-
APPLIED CATALYSIS B-ENVIRONMENTAL
nr 224,
strony 451 - 468,
ISSN: 0926-3373 - Język:
- angielski
- Rok wydania:
- 2018
- Opis bibliograficzny:
- Krukowska A., Winiarski M., Strychalska-Nowak J., Klimczuk T., Lisowski W., Mikolajczyk A., Pinto H., Puzyn T., Grzyb T., Zaleska-Medynska A.: Rare earth ions doped K 2 Ta 2 O 6 photocatalysts with enhanced UV–vis light activity// APPLIED CATALYSIS B-ENVIRONMENTAL. -Vol. 224, (2018), s.451-468
- DOI:
- Cyfrowy identyfikator dokumentu elektronicznego (otwiera się w nowej karcie) 10.1016/j.apcatb.2017.10.061
- Źródła finansowania:
-
- Działalność statutowa/subwencja
- Weryfikacja:
- Politechnika Gdańska
wyświetlono 135 razy
Publikacje, które mogą cię zainteresować
Monometallic nanoparticles decorated and rare earth ions doped KTaO3/K2Ta2O6 photocatalysts with enhanced pollutant decomposition and improved H2 generation
- A. Krukowska,
- G. Trykowski,
- W. Lisowski
- + 3 autorów
Lanthanide co-doped TiO2: the effect of metal type and amount on surface properties and photocatalytic activity
- J. Reszczyńska,
- T. Grzyb,
- J. W. Sobczak
- + 4 autorów
Visible light activity of rare earth metal doped (Er3+, Yb3+ or Er3+/Yb3+) titania photocatalysts
- J. Reszczyńska,
- T. Grzyb,
- J. W. Sobczak
- + 4 autorów
Preparation and photocatalytic activity of Nd-modified TiO2 photocatalysts: Insight into the excitation mechanism under visible light
- P. Parnicka,
- P. Mazierski,
- T. Grzyb
- + 6 autorów